Steel Wire is one of the four major types of steel plates, tubes, shapes and wires. It is made of hot-rolled wire rods and cold-drawn Steel Wires
Reworked products made of steel wire. Classified by cross-sectional shape, there are mainly round, square, rectangular, triangular, elliptical, flat, trapezoidal, Z-shaped, etc.; classified by size, there are extra fine <0.1 mm, thinner 0.1~0.5 mm, thin 0.5~1.5 mm, medium 1.5~3.0 mm, thick 3.0~6.0 mm, thicker 6.0~8.0 mm, extra thick >8.0 mm; classified by strength, there are low strength <390 MPa, lower strength 390~785 MPa, normal strength 785~1225 MPa, higher strength 1225~1960 MPa, high strength 1960~3135 MPa, extra high strength >3135 MPa; classified by use: ordinary quality steel wire including welding rod, nail making, net making, packaging and printing industry Steel wire, steel wire for cold upsetting for cold upsetting rivets, screws, etc. Steel for electrical purposes includes Special Steel wire for the production of overhead communication lines, steel-cored aluminum stranded wire, etc. Steel wire for textile industry includes rough combs, healds 013, card clothing and needles Steel wire, rope-making steel wire is specially used for the production of steel wire rope and spokes, Spring Steel wire includes steel wire for springs and spring washers, steel wire for pianos, tires, cords and transport belts, structural steel wire refers to watch industry, balls, steel wire for easy cutting of automatic machines, Stainless Steel Wire Including Stainless Steel Wires for the above purposes and surgical implant wires, resistance alloy wires for heater elements and resistance elements, and tool steel wires including steel wires for steel bars and steel wires for shoemaking.
Production process editing broadcast
The main process of steel wire production includes raw material selection, iron scale removal, drying, coating treatment, heat treatment, wire drawing, coating treatment, etc.
For raw material selection, see steel wire raw materials.
Removal of iron oxide scale refers to the removal of iron oxide scale on the surface of wire rod or intermediate wire billet, the purpose is to prevent the oxide scale from damaging the surface of the mold and steel wire during drawing, to prepare good surface conditions for subsequent coating or plating treatment and to reduce friction during drawing Reduce pullout force. There are two types of methods for removing iron scale, chemical method and mechanical method, see chemical descaling of wire rod and mechanical descaling of wire rod.
Main Specifications:
Maximum test force: 10kN
Measuring range: 2%-100% of the maximum test force (0.4%-100%FS can be selected)
Testing machine precision level: Level 1
Test force accuracy: better than ±1% of the indicated value
Beam displacement measurement: resolution is 0.01mm
Deformation accuracy: better than ±1%
Speed range: 0.01-500mm/min
Test space: 600mm
Host form: portal frame structure
Host size: 720×500×1820
Weight: about 500Kg
Working environment: room temperature ~ 45 ℃, humidity 20% ~ 80%